Method for Forming Thermoplastic Composites

ABSTRACT

A method for forming thermoplastic composites comprising: (a). cutting a thermoplastic film and a cloth material, wherein the thermoplastic film is comprised of a surface layer and an adhesive layer, and a melting point of the surface layer is higher than the adhesive layer; (b). placing the thermoplastic film on a platform of a molding machine, facing the adhesive layer upwardly, and covering the cloth material on the thermoplastic film, wherein the platform includes a plurality of channels defined therein, a plurality of concave and convex patterns arranged on a top surface thereof, and plural pores evenly formed on the top surface thereof and communicating with the plurality of channels; (c). heating the thermoplastic film by using a heating unit so as to melt the adhesive layer and to soften the surface layer.

FIELD OF THE INVENTION

The present invention relates to a method for forming thermoplastic composites in which the cloth material and the thermoplastic film are combined tighter to form the thermoplastic composites with a varying shape so as to produce shoes, purses, and hats further.

BACKGROUND OF THE INVENTION

A conventional method for forming thermoplastic composites is disclosed in TW Publication No. 1269703, wherein the film layer, the thermoplastic film, and fabric are rolled by two rollers together to form three-dimensional patterns, but the three-dimensional patterns are not obvious.

Another conventional method for forming thermoplastic composites is disclosed in TW Publication No. 1266693, wherein the cloth material and the thermoplastic film are hot pressed by an upper mold and a lower mild, yet concave and convex patterns on the upper mold and the lower mold are not three-dimensional obviously.

The present invention has arisen to mitigate and/or obviate the afore-described disadvantages.

SUMMARY OF THE INVENTION

The primary object of the present invention is to provide a method for forming thermoplastic composites in which the cloth material and the thermoplastic film are combined tighter to form the thermoplastic composites with a varying shape so as to produce shoes, purses, and hats further.

To obtain the above objective, a method for forming thermoplastic composites according to a first embodiment of the present invention contains steps of:

(a). cutting a thermoplastic film and a cloth material, wherein the thermoplastic film is comprised of a surface layer and an adhesive layer, and a melting point of the surface layer is higher than the adhesive layer;

(b). placing the thermoplastic film on a platform of a molding machine, facing the adhesive layer upwardly, and covering the cloth material on the thermoplastic film, wherein the platform includes a plurality of channels defined therein, a plurality of concave and convex patterns arranged on a top surface thereof, and plural pores evenly formed on the top surface thereof and communicating with the plurality of channels;

(c). heating the thermoplastic film by using a heating unit so as to melt the adhesive layer and to soften the surface layer, wherein air in the plurality of channels is drawn by a vacuum unit, and a top surface of the cloth layer is pressed by a pressing member, the plural pores draws the thermoplastic film and the cloth material downwardly, and the pressing member presses the cloth material, such that the adhesive layer of the thermoplastic film penetrates into the cloth material, the adhesive layer adheres with the cloth material, the surface layer of the thermoplastic film corresponds to the plurality of concave and convex patterns of the platform, thus forming three-dimensional patterns.

To obtain the above objective, a method for forming thermoplastic composites according to a second embodiment of the present invention contains steps of:

(a). cutting a thermoplastic film and a cloth material, wherein the thermoplastic film is comprised of a surface layer and an adhesive layer, and a melting point of the surface layer is higher than the adhesive layer;

(b). placing the cloth material on a platform of a molding machine, and then putting an adhesive layer of the thermoplastic film on the cloth material, wherein the platform includes a plurality of channels 31 defined therein, and plural pores evenly formed on the top surface thereof and communicating with the plurality of channels;

(c). heating the thermoplastic film by using a heating unit so as to melt the adhesive layer, wherein air in the plurality of channels is drawn by a vacuum unit, and a top surface of the thermoplastic film is pressed by a pressing member, the plural pores draw the thermoplastic film and the cloth material downwardly, and the pressing member presses the thermoplastic film, such that the adhesive layer of the thermoplastic film penetrates into the cloth material.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow chart of a method for forming thermoplastic composites according to a first embodiment of the present invention.

FIG. 2 is an amplified cross sectional view showing a thermoplastic film of the method for forming thermoplastic composites according to the first embodiment of the present invention.

FIG. 3 is a perspective view showing the operation of the method for forming thermoplastic composites according to the first embodiment of the present invention.

FIG. 4 is a cross sectional view showing the operation of the method for forming thermoplastic composites according to the first embodiment of the present invention.

FIG. 5 is a perspective view showing a finished product formed by the method for forming thermoplastic composites according to the first embodiment of the present invention.

FIG. 6 is a flow chart of a method for forming thermoplastic composites according to a second embodiment of the present invention.

FIG. 7 is a cross sectional view showing the operation of the method for forming thermoplastic composites according to the second embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

With reference to FIGS. 1-5, a method for forming thermoplastic composites according to a first embodiment of the present invention contains steps of:

(a). cutting a thermoplastic film 10 and a cloth material 20, wherein a size of the thermoplastic film 10 is less than that of the cloth material 20, and the thermoplastic film 10 is made of thermoplastic polymeric material and colorant by ways of an extruder, and the thermoplastic polymeric material is selected from TPU+SBR, TPU+SEBS, TPU+TPR, TPU+EPDM, TPU+TPU hot melt adhesives and TPU+Nylon elastomer, and wherein a color is printed, coated or surface sandwiched on the thermoplastic film 10, a thickness of the thermoplastic film 10 is 0.05 to 2.5 mm, the thermoplastic film 10 is comprised of a surface layer 11 and an adhesive layer 12 (as shown in FIG. 2), wherein a melting point of the surface layer 11 is 5° C. higher than the adhesive layer 12, and the cloth material is selected from woven, knitted fabrics, non-woven and sandwich mesh;

(b). placing the thermoplastic film 10 on a platform 30 of a molding machine, facing the adhesive layer 12 upwardly, and covering the cloth material 20 on the thermoplastic film 10 (as illustrated in FIG. 3), wherein the platform 30 includes a plurality of channels 31 defined therein, a plurality of concave and convex patterns 32 arranged on a top surface thereof, and plural pores 33 evenly formed on the top surface thereof and communicating with the plurality of channels 31, wherein the concave and convex patterns 3 are the same or varying, and a diameter of each pore is 0.001 mm;

(c). heating the thermoplastic film 10 by using a heating unit 40 so as to melt the adhesive layer 12 and to soften the surface layer 11, wherein air in the plurality of channels 34 is drawn by a vacuum unit 34, and a top surface of the cloth layer 20 is pressed by a pressing member 50, wherein the pressing member 50 has an air insulation film 51 and a press mold 52, a melting point of the air insulation film 51 is higher than that of the surface layer 11, and the air insulation film 51 is made of rubber or silicone, and the air insulation film 51 is covered on the platform 30 and the cloth material 20, the press mold 52 is pressed on the air insulation film 51.

Thereby, when the vacuum unit 34 operates, a pressure between the top surface of the platform 30 and the gas insulation film 51 is lower than atmospheric pressure and is a negative pressure to draw the gas insulation film 51 downwardly so that the gas insulation film 51 presses the cloth material 20, and the press mold 52 presses the gas insulation film 51, such that the adhesive layer 12 of the thermoplastic film 10 penetrates into the cloth material 20, hence the adhesive layer 12 adheres with the cloth material 20. In addition, the plural pores 33 draw the thermoplastic film 10 and the cloth material 20 downwardly, such that the surface layer 11 of the thermoplastic film 10 corresponds to the plurality of concave and convex patterns 32 of the platform 30, thus forming three-dimensional patterns obviously (as shown in FIG. 5). Also, the cloth material 20 and the thermoplastic film 10 are combined tighter to form the thermoplastic composites with a varying shape so as to produce shoes, purses, and hats further.

It is to be noted that the pressing member 50 is comprises of the air insulation film 51 or the press mold 52. For example, when gaps of the cloth material 20 are large, the pressing member 50 is the air insulation film 51, and the heating unit 40 is fixed in the platform 30 or the press mold 52.

Referring to FIGS. 6 and 7, a method for forming thermoplastic composites according to a second embodiment of the present invention contains steps of:

(a). cutting a thermoplastic film 10 and a cloth material 20;

(b). placing the cloth material 20 on a platform 30 of a molding machine, and then putting an adhesive layer 12 of the thermoplastic film 10 on the cloth material 20, wherein the platform 30 includes a plurality of channels 31 defined therein and plural pores 33 evenly formed on the top surface thereof and communicating with the plurality of channels 31;

(c). heating the thermoplastic film 10 by using a heating unit 40 so as to melt the adhesive layer 12, wherein air in the plurality of channels 34 is drawn by a vacuum unit 34, and a top surface of the thermoplastic film 10 is pressed by a pressing member 50.

Thereby, when the vacuum unit 34 operates, a pressure between the top surface of the platform 30 and the gas insulation film 51 is lower than atmospheric pressure and is a negative pressure to draw the gas insulation film 51 downwardly so that the gas insulation film 51 presses the thermoplastic film 10, and the press mold 52 presses the gas insulation film 51, the plural pores 33 draw the thermoplastic film 10 and the cloth material 20 downwardly, such that the adhesive layer 12 of the thermoplastic film 10 penetrates into the cloth material 20, hence the adhesive layer 12 adheres with the cloth material 20. In addition, the cloth material 20 and the thermoplastic film 10 are combined tighter to form the thermoplastic composites with a varying shape so as to produce shoes, purses, and hats further.

It is to be noted that the pressing member 50 is comprises of the air insulation film 51 or the press mold 52. For example, when gaps of the cloth material 20 are large, the pressing member 50 is the air insulation film 51, and the heating unit 40 is fixed in the platform 30 or the press mold 52.

While the preferred embodiments of the invention have been set forth for the purpose of disclosure, modifications of the disclosed embodiments of the invention as well as other embodiments thereof may occur to those skilled in the art. Accordingly, the appended claims are intended to cover all embodiments which do not depart from the spirit and scope of the invention. 

What is claimed is:
 1. A method for forming thermoplastic composites comprising: (a). cutting a thermoplastic film and a cloth material, wherein the thermoplastic film is comprised of a surface layer and an adhesive layer, and a melting point of the surface layer is higher than the adhesive layer; (b). placing the thermoplastic film on a platform of a molding machine, facing the adhesive layer upwardly, and covering the cloth material on the thermoplastic film, wherein the platform includes a plurality of channels defined therein, a plurality of concave and convex patterns arranged on a top surface thereof, and plural pores evenly formed on the top surface thereof and communicating with the plurality of channels; (c). heating the thermoplastic film by using a heating unit so as to melt the adhesive layer and to soften the surface layer, wherein air in the plurality of channels is drawn by a vacuum unit, and a top surface of the cloth layer is pressed by a pressing member, the plural pores draws the thermoplastic film and the cloth material downwardly, and the pressing member presses the cloth material, such that the adhesive layer of the thermoplastic film penetrates into the cloth material, the adhesive layer adheres with the cloth material, the surface layer of the thermoplastic film corresponds to the plurality of concave and convex patterns of the platform, thus forming three-dimensional patterns.
 2. A method for forming thermoplastic composites comprising steps of: (a). cutting a thermoplastic film and a cloth material, wherein the thermoplastic film is comprised of a surface layer and an adhesive layer, and a melting point of the surface layer is higher than the adhesive layer; (b). placing the cloth material on a platform of a molding machine, and then putting an adhesive layer of the thermoplastic film on the cloth material, wherein the platform includes a plurality of channels 31 defined therein, and plural pores evenly formed on the top surface thereof and communicating with the plurality of channels; (c). heating the thermoplastic film by using a heating unit so as to melt the adhesive layer, wherein air in the plurality of channels is drawn by a vacuum unit, and a top surface of the thermoplastic film is pressed by a pressing member, the plural pores draw the thermoplastic film and the cloth material downwardly, and the pressing member presses the thermoplastic film, such that the adhesive layer of the thermoplastic film penetrates into the cloth material.
 3. The method for forming thermoplastic composites as claimed in claim 1, wherein the pressing member is a press mold.
 4. The method for forming thermoplastic composites as claimed in claim 2, wherein the pressing member is a press mold.
 5. The method for forming thermoplastic composites as claimed in claim 3, wherein the heating unit is a press mold.
 6. The method for forming thermoplastic composites as claimed in claim 4, wherein the heating unit is a press mold.
 7. The method for forming thermoplastic composites as claimed in claim 3, wherein the heating unit is a platform.
 8. The method for forming thermoplastic composites as claimed in claim 4, wherein the heating unit is a platform.
 9. The method for forming thermoplastic composites as claimed in claim 3, wherein the pressing member is an air insulation film, and a melting point of the air insulation film is higher than the surface layer and is covered on the platform.
 10. The method for forming thermoplastic composites as claimed in claim 4, wherein the pressing member is an air insulation film, and a melting point of the air insulation film is higher than the surface layer and is covered on the platform.
 11. The method for forming thermoplastic composites as claimed in claim 3, wherein the pressing member includes an air insulation film and a press mold, and a melting point of the air insulation film is higher than the surface layer and is covered on the platform, the press mold presses on the air insulation film.
 12. The method for forming thermoplastic composites as claimed in claim 4, wherein the pressing member includes an air insulation film and a press mold, and a melting point of the air insulation film is higher than the surface layer and is covered on the platform, the press mold presses on the air insulation film.
 13. The method for forming thermoplastic composites as claimed in claim 1, wherein the thermoplastic film is made of thermoplastic polymeric material and colorant by ways of an extruder.
 14. The method for forming thermoplastic composites as claimed in claim 2, wherein the thermoplastic film is made of thermoplastic polymeric material and colorant by ways of an extruder.
 15. The method for forming thermoplastic composites as claimed in claim 1, wherein the thermoplastic polymeric material is selected from TPU+SBR, TPU+SEBS, TPU+TPR, TPU+EPDM, TPU+TPU hot melt adhesives and TPU+Nylon elastomer.
 16. The method for forming thermoplastic composites as claimed in claim 2, wherein the thermoplastic polymeric material is selected from TPU+SBR, TPU+SEBS, TPU+TPR, TPU+EPDM, TPU+TPU hot melt adhesives and TPU+Nylon elastomer.
 17. The method for forming thermoplastic composites as claimed in claim 1, wherein a color is printed, coated or surface sandwiched on the thermoplastic film.
 18. The method for forming thermoplastic composites as claimed in claim 1, wherein a color is printed, coated or surface sandwiched on the thermoplastic film. 